S10C low mechanical strength, plasticity, toughness, and easy to mold in cold state, easy cutting, welding performance, in order to improve the surface hardness can be carburizing and cyanidation. S10C for the manufacture of low-strength welding parts, cold stamping parts, forgings and carburizing parts such as bolts, washers, partitions, shell and so on.
S10C Chemical composition:
C: 0.08 - 0.13
Si: 0.15 - 0.35
Mn: 0.30 - 0.60
S: ≤ 0.030
P: ≤0.030
Cr: ≤0.20
Cu: ≤ 0.25
C: 0.08 - 0.13
Si: 0.15 - 0.35
Mn: 0.30 - 0.60
S: ≤ 0.030
P: ≤0.030
Cr: ≤0.20
Cu: ≤ 0.25
S10C Mechanical properties:
Tensile strength σb (MPa): ≥335 (34)
Yield strength σs (MPa): ≥205 (21)
Elongation δ5 (%): ≥31
Sectional shrinkage ψ (%): ≥55
Hardness: no heat treatment, ≤ 137HB
Sample size: The sample size was 25 mm
Tensile strength σb (MPa): ≥335 (34)
Yield strength σs (MPa): ≥205 (21)
Elongation δ5 (%): ≥31
Sectional shrinkage ψ (%): ≥55
Hardness: no heat treatment, ≤ 137HB
Sample size: The sample size was 25 mm
S10C Application:
Used in manufacture high toughness and low load parts, such as chuck, tube, washer, friction lining, dust cover, container, deep drawing vessels, enamelware, bearing grinding shelf, cold heading bolt and nut, etc. Also can used in manufacture carburizing parts, such gear, roller, sleeve, plow, etc.
Used in manufacture high toughness and low load parts, such as chuck, tube, washer, friction lining, dust cover, container, deep drawing vessels, enamelware, bearing grinding shelf, cold heading bolt and nut, etc. Also can used in manufacture carburizing parts, such gear, roller, sleeve, plow, etc.